TOKYO, Jan 10 – Tanaka Holdings Co., Ltd. (Head office: Chiyoda-ku, Tokyo; Representative Director and CEO: Akira Tanae) announces the start of sample shipments of SJeva, a newly-developed, high-quality Au deposition material, by Tanaka Kikinzoku Kogyo K.K (Head office: Chiyoda-ku, Tokyo; Representative Director and CEO: Akira Tanae).
Tanaka Kikinzoku Kogyo conducts industrial business within the Tanaka Precious Metals. The new deposition material has higher purity than earlier products, making it possible to reduce the amount of precious metals used, increase productivity and cut costs by reducing processing, and raise recoverability and recyclability.
By improving manufacturing methods, Tanaka Kikinzoku Kogyo successfully reduced the amount of non-metallic inclusions in the deposition material compared to conventional materials. Tanaka Kikinzoku Kogyo previously handled Au deposition materials with a purity of 4N (99.99% gold content) to 5N (99.999% gold content), and the new deposition material enhances the lineup of high-quality products.
By using a deposition material with extremely low non-metallic inclusions, contaminants that collect on the surface during melting of the deposition material are reduced, eliminating the need for cleaning. The high-purity deposition material also makes it possible to shorten the preheating time before film formation, decreasing consumption of deposition material that does not contribute to film formation and reducing costs.
In addition, the new deposition material contains low levels of gas, and as a result, a reduction in splash phenomenon from the deposition source during film formation can be expected, and it is possible to reduce the number of particles that form on substrates, even during high-rate deposition.
As a result of the above properties and benefits of the new deposition material, it is expected to contribute to higher end-user productivity and lower costs when manufacturing final products that use deposition materials such as micro-wiring and MEMS in the semiconductor fields as well as optical devices, LEDs, and medical equipment.
Benefits of the New Deposition Material
– Reduced number of cleaning processes
Usually, various shapes of deposition materials including pellet, plate, ribbon, wire, and grain shapes are used depending on the application, and melting is always necessary during deposition.
Non-metallic inclusions present in the deposition material condense and form impurities during melting, and as a result, a cleaning process is essential. The new deposition material, however, contains an extremely low level of impurities, eliminating the need for a cleaning process, which is expected to reduce the number of processes.
– Costs reduced through shorter preheating time before film formation
A high-purity deposition material makes it possible to reduce the preheating time before film formation, which reduces consumption of deposition material that does not contribute to film formation and can reduce costs.
– Splash phenomenon from deposition source during film formation curtailed, reducing particle formation on substrates during high-rate deposition
The splash phenomenon is a representative type of problem that occurs during deposition that causes flaws such as particles and pin holes on substrates and films. High productivity can be expected from film formation with a higher deposition rate, but the more the deposition rate is increased, the more likely splash phenomenon is to occur, presenting a problem. The cause is gas present in the deposition material, and Tanaka Kikinzoku Kogyo successfully reduced the amount of gas by improving the manufacturing process, and as a result, splash phenomenon control effects can be expected.